Aluminum Strip Sheet Used in Air Cooling Fin Material for Tubes

Model NO.: 1060, 1100
Place of Origin: Zhengzhou China (Mainland)
Port of Loading: Qingdao,Shanghai
Trademark: Signi Aluminium
Transport Package: Carton Box
Specification: CE
Origin: Henan China
HS Code: 760700900
Aluminum strip sheet used in air cooling fin material for tubes 

*Good consistency for any fin mill
*Good mechanical property and surface condition 

Aluminium brazing material production
 
Complex assemblies can be turned into single unit by just one pass through a brazing furnace. Aluminium brazing facilitates the joining of parts with a near-eutectic Ai-Si filler alloy, the liquid temperature which is about 50 ºC lower than that of the core. In serial heat exchanger production the filler alloy is supplied via a thin clad on a core alloy.
 
Compound Material
 
Aluminium brazing material is a sophisticated multi-layer compound consisting of a core alloy which provides the stength and life cycle requirements of the heat exchanger and a clad brazing filler. A one-sided protection layer can also be clad, in order to prevent water-side radiator corrosion.
 
During brazing, only the clad brazing alloy melts, while the core alloys remain solid. The design and the applied materials of the heat exchanger are adjusted to optimize the brazing result regarding the required post braze mechanical properties as well as the corrosion resistance.
 
Roll cladding
 
Today, two basic cladding techniques, roll bonding and cast cladding, have become established industrially. Roll cladding is a solid-state welding process, which is used to join similar and dissimilar aluminium alloys, and represents the primary method of manufacturing fuselage skin sheet for aircraft, bright products and brazing sheet for automotive applications. The cladding layers are attached to the core slab by welding and metallurgical bonding using hot rolling. The cast cladding technique is based on a conventional direct chill mould modified in order to allow multiple metal streams to be casted into one single ingot.
 
Cladding thickness
 
Signi's well established, roll bonding process guarantees tight cladding thickness tolerances, which are essential for ensuring stable brazing results. Rather thin clad layers of 5% can be manufactured, as well as brazing materials also with a cladding thickness of 20%.
 
 
Aluminum Strip Sheet Used in Air Cooling Fin Material for Tubes
 
Aluminum Strip Sheet Used in Air Cooling Fin Material for Tubes
Aluminum Strip Sheet Used in Air Cooling Fin Material for Tubes
Performance index of aluminium air cooling fin material 
 
Alloy
 		 Temper
 		 Thickness
(mm)
 		 Tolerance
(mm)
 		 Clad rate(%)
 		 Mechanical property
 
          Tensile Strength
(MPa)
 		 Yield
Strength
(MPa)
 		 Elongation
Min.(%)
 
1060 O 0.35~0.40 ±0.02 None 55~95 ≥15 25
1100 O 0.35~0.40 ±0.02 None 75~105 ≥25 25
*Alloy\specification and mechanical property can be customized according to different requirement. 

DELCO Starter: PMGR, PG260, PG260M, PG260F, 28MT, 29MT, 40MT, 42MT, 41MT, 50MT,


POINTS TO ATTENTION:

1- Keep a careful check on gear ring before installation, replace one if damages.

2-Installed surface of both motor and generator should be kept clean, Make sure the strength to the bolts.

3- Clean each connection port, Strictly observed the sketch, Make sure of firm connection and tight electric conduction.

4- Check if the key could be automatic(Electrical Starter).


DELCO Starter

DELCO Starter, DELCO Starter Parts, DELCO Starter Motor,Electrical Starter

NINGBO ZHONGWANG AUTO FITTINGS CO.,LTD , http://www.autostarter-alternator.com